牌号
Brand
|
型号
Model
|
线径
Wire
Diameter
|
保护气体
Shielding Gas
|
熔敷金属化学成分(%)
Chemical Composition of Deposited Metal
|
用途
Applications
|
|
GB
|
JIS
|
AWS
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
Cu
|
Other
|
|
YA308(Q)
|
E308T1-1
|
YF308C
|
E308T1-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0-11.0
|
0.75
|
0.75
|
|
用于焊接18%Cr、8%Ni钢，具有良好的抗热裂性。
Be used to weld 18%Cr, 8%Ni steels, better heat-resistance crack-resistance。
|
|
YA308L(Q)
|
E308LT1-1
|
YF308LC
|
E308LT1-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0-11.0
|
0.75
|
0.75
|
|
用于焊接低碳18%Cr、8%Ni钢，耐裂性与耐蚀性均甚优良。
Be used to weld low-carbon 18%Cr, 8%Ni steels，better crack-resistance corrosion-resistance.
|
|
YA309(Q)
|
E309T0-1
|
YF309C
|
E309T0-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.12
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0-14.0
|
0.75
|
0.75
|
|
用于22%Cr、12%Ni钢，以及软钢与不锈钢，铬钼钢等异种金属的焊接，耐热性与耐蚀性甚为优越。
Be used to weld 22%Cr, 12%Ni steels,and soft steel and stainless steel,chromium molybdenum steel,different race welding of metals,heat-resistance,corrosion-resistance bear the eclipse even superior.
|
|
YA309L(Q)
|
E309LT0-1
|
YF309LC
|
E309LT0-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0-14.0
|
0.75
|
0.75
|
|
用于低碳22%Cr、12%Ni钢，以及软钢与不锈钢，铬钼钢等异种金属的焊接，耐热性与耐蚀性甚为优越。
Be used to weld low-carbon 22%Cr, 12%Ni steels,and soft steel and stainless steel,chromium molybdenum steel,different race welding of metals,heat-resistance, corrosion-resistance bear the eclipse even superior.
|
|
YA309MoL(Q)
|
E309LMoT0-1
|
YF309MoLC
|
E309LMoT0-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.035
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0-14.0
|
2.0-3.0
|
0.75
|
|
用于低碳22%Cr、12%Ni、2％Ｍo钢，以及软钢与不锈钢，铬钼钢等异种金属的焊接，耐热性与耐蚀性甚为优越。
Be used to weld low-carbon 22%Cr, 12%Ni 2％Ｍo steels,and soft steel and stainless steel,chromium molybdenum steel,different race welding of metals,heat-resistance,corrosion-resistance bear the eclipse even superior.
|
|
YA316(Q)
|
E316T0-1
|
YF316C
|
E316T0-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0-14.0
|
2.0-3.0
|
0.75
|
|
用于18%Cr、12%Ni、2％Ｍo钢，其耐裂性、耐蚀性皆佳。
Be used to weld 18%Cr, 12%Ni, 2％Ｍo steels, its crack-resistance,corrosion-resistance more superior.
|
|
YA316L(Q)
|
E316LT0-1
|
YF316LC
|
E316LT0-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0-14.0
|
2.0-3.0
|
0.75
|
|
用于低碳18%Cr、12%Ni、2％Ｍo钢，耐蚀性更为优越。
Be used to weld low-carbon 18%Cr, 12%Ni, 2％Ｍo steels, its corrosion-resistance more superior.
|
|
YA317L(Q)
|
E317LTO-1
|
YF317LC
|
E317LTO-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.5-20.5
|
13.0-15.0
|
3.0-4.0
|
0.75
|
|
含较高的Ｍo及极低的碳，高温时仍具有高强度，对于硫酸、亚硫酸、有机酸等防蚀性有极佳的效果。
Contain the higher Mo and very the low carbon,heat hour still have the high strength,and defent the eclipse to have for sulfuric acid,sulfurous acid,organic acid¡etc.very good result.
|
|
YA347(Q)
|
E347T1-1
|
YF347C
|
E347T1-1
|
1.2-1.6
|
CO2(or)
Ar+(20-25)%CO2
|
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.0-21.5
|
9.0-11.0
|
0.75
|
0.75
|
Nb:10×C-1.0
|
含Ｎb，增加了粒间腐蚀的防蚀性，高温时强度大，适于耐热钢的焊接。
Contain the Nb, and increase the grain to decay of defend the eclipse,heat the hour strength big,used for the welding of heat-proof steel.
|
|
YA410(Q)
|
E410T0-1
|
YF410C
|
E410T0-1
|
1.2-1.6
|
CO2
|
0.12
|
0.5
|
0.6
|
0.03
|
0.03
|
11.5-13.5
|
0.6
|
0.75
|
0.75
|
|
用于13％Cr的马氏体不锈钢焊接，耐磨性及耐蚀性良好。
Be used to weld 13%Cr martensitic stainless steels,better whet-resistance and corrosion resistance.
|
|