牌 号 Brand |
型 号 Model |
线径 Wire Diameter |
保护气体 Shielding Gas |
熔敷金属化学成分(%) Chemical Composition of Deposited Metal |
用 途 Applications |
|||||||||||
GB
|
JIS
|
AWS
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
Cu
|
Other
|
||||
ER308
|
H08Cr21Ni10Si
|
Y308
|
ER308
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0-11.0
|
0.75
|
0.75
|
|
用于焊接18%Cr、8%Ni钢,具有良好的抗热裂性。 Be used to weld 18%Cr, 8%Ni steels,better heat-resistance crack-resistance。 |
ER308L
|
H03Cr21Ni10Si
|
Y308L
|
ER308L
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0-11.0
|
0.75
|
0.75
|
|
用于焊接低碳18%Cr、8%Ni钢,耐裂性与耐蚀性均甚优良。 Be used to weld low£carbon 18%Cr, 8%Ni steels,better crack-resistance corrosion-resistance. |
ER308LSi
|
H03Cr21Ni10Si1
|
Y308LSi
|
ER308LSi
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.03
|
0.65-1.0
|
1.0-2.5
|
0.03
|
0.03
|
19.5-22.0
|
9.0-11.0
|
0.75
|
0.75
|
|
熔敷金属流动性较308L为佳,在焊接操作上也更优越。 Deposited metal fluidity better than 308L, on weld the operation too more superior. |
ER309
|
H12Cr24Ni13Si
|
Y309
|
ER309
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.12
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0-14.0
|
0.75
|
0.75
|
|
用于22%Cr、12%Ni钢,以及软钢与不锈钢,铬钼钢等异种金属的焊接,耐热性与耐蚀性甚为优越。 Be used to weld 22%Cr, 12%Ni steels,and soft steel and stainless steel,chromium molybdenum steel, different race welding of metals,heat-resistance,corrosion-resistance bear the eclipse even superior. |
ER309L
|
H03Cr24Ni13Si
|
Y309L
|
ER309L
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
23.0-25.0
|
12.0-14.0
|
0.75
|
0.75
|
|
用于低碳22%Cr、12%Ni钢,以及软钢与不锈钢,铬钼钢等异种金属的焊接,耐热性与耐蚀性甚为优越。 Be used to weld low-carbon 22%Cr, 12%Ni steels,and soft steel and stainless steel,chromium molybdenum steel, different race welding of metals, heat-resistance,corrosion-resistance bear the eclipse even superior. |
ER310
|
H12Cr26Ni21Si
|
Y310
|
ER310
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.08-0.15
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
25.0-28.0
|
20.0-22.5
|
0.75
|
0.75
|
|
用于25%Cr、20%Ni钢,硬化性高的钢材以及异种金属的焊接。 Be used to weld 25%Cr, 20%Ni steels, hardening welding of high steel material and different race metals. |
ER312
|
H15Cr30Ni9
|
Y312
|
ER312
|
0.6-4.0
|
Ar Ar+0.5-2%CO2
|
0.15
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
28.0-32.0
|
8.0-10.5
|
0.75
|
0.75
|
|
用于29%Cr、9%Ni钢以及异种金属的焊接。其耐裂性更为优越。 Be used to weld 29%Cr, 9%Ni steels, and different race metals,its crack-resistance more superior. |
ER316
|
H08Cr19Ni12Mo2Si
|
Y316
|
ER316
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0-14.0
|
2.0-3.0
|
0.75
|
|
用于18%Cr、12%Ni、2%Mo钢,其耐裂性、耐蚀性皆佳。 Be used to weld 18%Cr, 12%Ni, 2%Mo steels, its crack-resistance,corrosion-resistance more superior. |
ER316L
|
H03Cr19Ni12Mo2Si
|
Y316L
|
ER316L
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0-14.0
|
2.0-3.0
|
0.75
|
|
用于低碳18%Cr、12%Ni、2%Mo钢,耐蚀性更为优越。 Be used to weld low-carbon 18%Cr, 12%Ni, 2%Mo steels, its corrosion-resistance more superior. |
ER316LSi
|
H03Cr19Ni12Mo2Si1
|
Y316LSi
|
ER316LSi
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.03
|
0.65-1.0
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0-14.0
|
2.0-3.0
|
0.75
|
|
熔敷金属流动性较316L为佳,在焊接操作上也更优越。 Deposited metal fluidity better than 316L, on weld the operation too more superior. |
ER317L
|
H03Cr19Ni14Mo3
|
Y317L
|
ER317L
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.03
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.5-20.5
|
13.0-15.0
|
3.0-4.0
|
0.75
|
|
含较高的Mo及极低的碳,高温时仍具有高强度,对于硫酸、亚硫酸、有机酸等防蚀性有极佳的效果。 Contain the higher Mo and very the low carbon,heat hour still have the high strength,and defent the eclipse to have for sulfuric acid,sulfurous acid,organic acid¡etc.very good result. |
ER318
|
H08Cr19Ni12Mo2Nb
|
Y318
|
ER318
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
18.0-20.0
|
11.0-14.0
|
2.0-3.0
|
0.75
|
Nb:8×C-1.0
|
含Mo及Nb,耐热性、耐蚀性、粒间腐蚀皆优越。对于硫酸、亚硫酸、有机酸等防蚀性有极佳的效果。 Contain the Mo and Nb,heat-proof,bear the eclipse,grain to decay all superior.defend to eclipse contain good result for sulfuric acid,sulfurous acid,organic acid¡etc. |
ER347
|
H08Cr20Ni10Nb
|
Y347
|
ER347
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.08
|
0.3-0.65
|
1.0-2.5
|
0.03
|
0.03
|
19.0-21.5
|
9.0-11.0
|
0.75
|
0.75
|
Nb:10×C-1.0
|
含Nb,增加了粒间腐蚀的防蚀性,高温时强度大,适于耐热钢的焊接。 Contain the Nb,and increase the grain to decay of defend the eclipse,heat the hour strength big,used for the welding of heat-proof steel. |
ER410
|
H12Cr13
|
Y410
|
ER410
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.12
|
0.5
|
0.6
|
0.03
|
0.03
|
11.5-13.5
|
0.6
|
0.75
|
0.75
|
|
用于13%Cr的马氏体不锈钢焊接,耐磨性及耐蚀性良好。 Be used to weld 13%Cr martensitic stainless steels,better whet-resistance and corrosion resistance. |
ER430
|
H10Cr17
|
Y430
|
ER430
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.10
|
0.5
|
0.6
|
0.03
|
0.03
|
15.5-17.0
|
0.6
|
0.75
|
0.75
|
|
用于SUS430的焊接,耐磨性及耐蚀性良好。 Be used to weld SUS430steels,better whet-resistance and corrosion resistance. |
ER630
|
H05Cr17Ni14Cu4Nb
|
Y630
|
ER630
|
0.6-4.0
|
Ar Ar+0.5-2%CO2 |
0.05
|
0.75
|
0.25-0.75
|
0.03
|
0.03
|
16.0-16.75
|
4.5-5.0
|
0.75
|
3.25-4.0
|
Nb:0.15-0.3
|
为析出硬化型不锈钢,耐磨性及耐蚀性良好。 Harden the type stainless steel,better whet-resistance and corrosion resistance. |